Перегляд за Автор "Voronov, D. L."
Зараз показуємо 1 - 4 з 4
Результатів на сторінці
Налаштування сортування
Документ Analysis of 46.9-nm Pulsed Laser Radiation Aftereffects in Sc/Si Multilayer X-Ray Mirrors(Springer, 2007) Pershyn, Yuriy P.; Voronov, D. L.; Zubarev, Evgeniy N.; Sevryukova, V. A.; Kondratenko, V. V.; Vaschenko, G.; Grisham, M.; Menoni, C. S.; Rocca, J. J.; Vinogradov, A.V.; Artyukov, I. A.; Uspenskii, Yu. A.Specific structural changes in Sc/Si multilayers (MLs) irradiated by nanosecond 46.9-nm single laser pulses with fluences of 0.04-5.00 J/cm2 were studied by methods of SEM and cross-sectional TEM. The threshold damage was found to be 0.08 J/cm2 The ML melts down under the fluence F >0.08 J/cm2 and the exothermic reaction of silicide formation starts. Main degradation mechanisms of MLs are discussed. The results of this study can be used for development of advanced multilayer mirrors capable handling the intense radiation conditions of new generation coherent X-ray sources.Документ The influence of working gas pressure on interlayer mixing in magnetron-deposited Mo/Si multilayers(American Institute of Physics, 2011) Pershyn, Yuriy P.; Gullikson, E. M.; Artyukov, I. A.; Kondratenko, V. V.; Sevryukova, V. A.; Voronov, D. L.; Zubarev, Evgeniy N.; Vinogradov, A. V.Impact of Ar gas pressure (1−4 mTorr) on the growth of amorphous interlayers in Mo/Si multilayers deposited by magnetron sputtering was investigated by small-angle x-ray scattering (l=0.154 nm) and methods of cross-sectional transmission electron microscopy. Some reduction of thickness of the amorphous inter-layers with Ar pressure increase was found, while composition of the layers was enriched with molybdenum. The interface modification resulted in raise of EUV reflectance of the Mo/Si multilayersДокумент Mechanisms of radiation damage to Sc/Si multilayer mirrors under EUV laser irradiation(IOP Publishing Ltd, 2009) Pershyn, Yuriy P.; Zubarev, Evgeniy N.; Voronov, D. L.; Sevryukova, V. A.; Kondratenko, V. V.; Vaschenko, G.; Grisham, M.; Menoni, C. S.; Rocca, J. J.; Artioukov, Y. A.; Uspenskii, Y. A.; Vinogradov, A . V.Specific structural changes in Sc/Si multilayer mirrors irradiated with extreme ultraviolet (EUV) laser single pulses (λ = 46.9 nm) at near damage threshold fluences (0.04–0.23 J cm−2) are analysed. We have identified melting of surface layers as the basic degradation mechanism for the mirrors. Both heat generation during silicide formation and low heat conduction of the layered system significantly decreases the degradation threshold of Sc/Si multilayer mirrors compared with bulk materials. The results are relevant to the use of the multilayer mirrors for shaping and directing the intense beams produced by the new generation of coherent EUV sourcesДокумент Structure, thermal stability and reflectivity of Sc/Si and Sc/W/Si/W multilayer X-ray mirrors(SPIE, 2001) Vinogradov, A. V.; Pershin, Yu. P.; Zubarev, Evgeniy N.; Voronov, D. L.; Pen’kov, A. V.; Kondratenko, V. V.; Uspenskii, Yu. A.; Artioukov, I. A.; Seely, J. F.Processes going on at elevated temperatures between Sc and Si layers in Sc/Si coatings are studied by X-ray scattering and cross-sectional transmission electron microscopy. It is shown that the W layers of 0.5-0.8nm placed at Sc-Si interfaces form effective barriers preventing the penetration of Si into Sc. The effects of Si-Sc diffusion and W-barriers on the reflectivity of coatings are calculated in good agreement with experimental results. Presented measurements show that the Sc/W/Si/W multilayers with the period of 20.5 nm fabricated by dc-magnetron sputtering possess thermal stability up to 250 C and the normal incidence reflectivity of 24% at wavelengths about 40 nm.