Please use this identifier to cite or link to this item: http://repository.kpi.kharkov.ua/handle/KhPI-Press/21278
Full metadata record
DC FieldValueLanguage
dc.contributor.authorСоболь, Олег Валентиновичru
dc.contributor.authorАндреев, Анатолий Афанасьевичru
dc.contributor.authorСтолбовой, Вячеслав Александровичru
dc.contributor.authorКнязев, Сергей Анатольевичru
dc.contributor.authorБармин, Александр Евгеньевичru
dc.contributor.authorКривобок, Н. А.ru
dc.date.accessioned2016-05-05T10:52:37Z-
dc.date.available2016-05-05T10:52:37Z-
dc.date.issued2016-
dc.identifier.citationИсследование влияния режимов ионного азотирования на структуру и твердость стали / О. В. Соболь [и др.] // Восточно-Европейский журнал передовых технологий = Eastern-Еuropean journal of enterprise technologies. – 2016. – № 2/5 (80). – C. 63-68.ru
dc.identifier.urihttp://repository.kpi.kharkov.ua/handle/KhPI-Press/21278-
dc.description.abstractИспользуя ионное азотирование при давлении PN=(4…40).10-4 Торр и постоянных отрицательных потенциалах –600, –900 и –1300 В, изучены возможности структурной инженерии и ее влияние на твердость. Выявлено образование S фазы при наименьшем давлении, определен ее период решетки 0,381 нм, что соответствует формуле FeN0,4, а также установлена большая ширина дифракционных рефлексов S фазы, что свидетельствует о дроблении и высокой микродеформации кристаллитов исходного аустенита при образовании S фазы. Показано, что наивысшую твердость можно получить при условии формирования в процессе азотирования композиции из CrN, S и исходной γ (аустенит) фаз.ru
dc.description.abstractApplication of low-temperature plasma nitriding of nonself-sustained arc low-pressure discharge allows solving a critical problem of increasing the stainless steel hardness and getting a wide range of structural states, including metastable at low temperatures, such as the S-phase (nitrided austenite). Using ion nitriding at a pressure of PN=(4…40)·10-4 Torr and constant negative potentials –600, –900 and –1300 V, the possibilities of structural engineering in the ion-induced surface modification and its influence on hardness are examined. When using ion nitriding regimes, the S-phase formation at the lowest pressure is revealed, the grating spacing of 0.381 nm is determined, which corresponds to the formula FeN0,4, and a large width of the diffraction reflections of the S-phase evidences fragmentation and high microstrain of the initial austenite in the S-phase formation. It is shown that the highest hardness can be obtained when the composition of CrN, S and the original austenitic phase is formed in the nitriding process, which is achieved under the following nitriding regimes: the pressure of 4·10-3 Torr and relatively low negative bias potential of 600 V.en
dc.language.isoru-
dc.publisherТехнологический центр, Украинский государственный университет железнодорожного транспортаru
dc.subjectионное азотированиеru
dc.subjectаустенитru
dc.subjectS фазаru
dc.subjectнитрид хромаru
dc.subjectдифракционные спектрыru
dc.subjection nitridingen
dc.subjectausteniticen
dc.subjectS phaseen
dc.subjectchromium nitrideen
dc.subjectdiffraction spectraen
dc.titleИсследование влияния режимов ионного азотирования на структуру и твердость сталиru
dc.title.alternativeStudy of the effect of ion nitriding regimes on the structure and hardness of steelen
dc.typeArticleen
dc.identifier.doi10.15587/1729-4061.2016.63659-
Appears in Collections:Кафедра "Матеріалознавство"

Files in This Item:
File Description SizeFormat 
2016_Sobol_Issledovanie_vliyaniya.pdf872,3 kBAdobe PDFThumbnail
View/Open
Show simple item record  Google Scholar



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.