Please use this identifier to cite or link to this item: http://repository.kpi.kharkov.ua/handle/KhPI-Press/53530
Full metadata record
DC FieldValueLanguage
dc.contributor.authorБорисенко, Оксана Миколаївнаuk
dc.contributor.authorЛогвінков, Сергій Михайловичuk
dc.contributor.authorШабанова, Галина Миколаївнаuk
dc.contributor.authorОстапенко, Ігор Анатолійовичuk
dc.contributor.authorШумейко, Віта Миколаївнаuk
dc.date.accessioned2021-07-13T10:53:31Z-
dc.date.available2021-07-13T10:53:31Z-
dc.date.issued2021-
dc.identifier.citationГеометро–топологічні характеристики субсолідусної будови системи МgО – Аl2 О3 – ТіО2 / О. М. Борисенко [та ін.] // Вісник Національного технічного університету "ХПІ". Сер. : Хімія, хімічна технологія та екологія = Bulletin of the National Technical University "KhPI". Ser. : Chemistry, Chemical Technology and Ecology : зб. наук. пр. – Харків : НТУ "ХПІ", 2021. – № 1 (5). – С. 18-23.uk
dc.identifier.urihttp://repository.kpi.kharkov.ua/handle/KhPI-Press/53530-
dc.description.abstractСеред матеріалів, що привертають велику увагу з точки зору створення вогнетривких виробів з підвищеною термостійкістю можна виділити матеріали на основі композицій системи MgO – Al2O3 –TiO2. В результаті проведеного термодинамічної аналізу системи MgO – Al2O3 –TiO2 встановлено, що розбиття системи на елементарні трикутники зазнає змін у трьох температурних інтервалах: I – до температури 1537 К, II – в температурному інтервалі 1537 – 2076 К та вище температури 2076 К. Встановлено, що до температури 2076 К існує концентраційна область шпінельних фаз: алюмомагнезіальна шпінель – кванділіт. Вище температури 1537 К існує концентраційна область: тіаліт – карроіт, яка відповідає вимогам до матеріалів з високою термостійкістю. Елементарний трикутник TiO2 – Al2TiO5 – MgTi2O5 можна використовувати для отримання термостійких матеріалів на основі Al2TiO5 стабілізованого MgTi2O5. Для отримання термостійких периклазошпінельних матеріалів рекомендовано елементарний трикутник Mg2TiO4 – MgAl2O4 – MgO, у якому присутні лише сполуки з кубічною кристалічною решіткою. Таким чином, розбиття системи MgO – Al2O3 –TiO2 на елементарні трикутники і аналіз геометро-топологічних характеристик фаз системи дозволило вибрати в досліджуваній системі області складів, що володіють оптимальними властивостями для отримання матеріалів з заданими оптимальними властивостями.uk
dc.description.abstractAmong the materials that attract attention from the point of view of creating refractory products with increased heat resistance, one can single out materials based on compositions of the MgO – Al2O3 –TiO2 system. As a result of the thermodynamic analysis of the MgO – Al2O3 –TiO2 system, it was found that the partition of the system into elementary triangles will change in three temperature ranges: I – up to 1537 K, II – in the temperature range 1537 – 2076 K and above 2076 K. It has been established that up to a temperature of 2076 K there is a concentration range of spinel phases: magnesium aluminate spinel –quandylite. Above 1537 K, there is a concentration range: tialite – karroite, which meets the requirements for materials with high heat resistance. The elementary triangle TiO2 – Al2TiO5 – MgTi2O5 can be used to obtain heat-resistant materials based on Al2TiO5 stabilized by MgTi2O5. To obtain heat-resistant periclase-spinel materials, an elementary triangle Mg2TiO4 – MgAl2O4 – MgO is recommended, in which only compounds with a cubic crystal lattice are present. Thus, the division of the MgO – Al2O3 –TiO2 system into elementary triangles and the analysis of the geometrical-topological characteristics of the phases of the system made it possible to select in the system under study the regions of compositions that have optimal properties for obtaining materials with the specified optimal properties.uk
dc.language.isouk-
dc.publisherНаціональний технічний університет "Харківський політехнічний інститут"uk
dc.subjectтіалітuk
dc.subjectкарроітuk
dc.subjectалюмомагнезіальна шпінельuk
dc.subjectкванділітuk
dc.subjecttialitеen
dc.subjectkarroiteen
dc.subjectmagnesium aluminate spinelen
dc.subjectquandiliteen
dc.titleГеометро–топологічні характеристики субсолідусної будови системи МgО – Аl2 О3 – ТіО2uk
dc.title.alternativeGeometrical–topological characteristics of the subsolidus structure in the МgО – Аl2О3 – ТiО2 systemen
dc.typeArticleen
dc.identifier.doidoi.org/10.20998/2079-0821.2021.01.03-
dc.identifier.orcidorcid.org/0000-0002-2746-6797-
dc.identifier.orcidorcid.org/0000-0001-5957-2386-
dc.identifier.orcidorcid.org/0000-0001-7204-940X-
dc.identifier.orcidorcid.org/0000-0003-0567-0946-
Appears in Collections:Вісник № 01. Хімія, хімічна технологія та екологія
Кафедра "Технологія кераміки, вогнетривів, скла та емалей"

Files in This Item:
File Description SizeFormat 
visnyk_KhPI_2021_1_CCTE_Borysenko_Heometro-topolohichni.pdf322,77 kBAdobe PDFThumbnail
View/Open
Show simple item record  Google Scholar



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.