Title: Исследование теплодеформационного влияния при поверхностном упрочнении сталей термофрикционной обработкой
Other Titles: Study of heat deformation influence in surface strain hardening of steel by thermofriction processing
Authors: Волков, Олег Алексеевич
Keywords: термофрикционная обработка; трение; упрочняющий диск; белый слой; наклеп; ε-карбид; наноструктура; thermofriction processing; friction; hardening disc; white layer; strain hardening; ε-carbide; nanostructure
Issue Date: 2016
Publisher: Технологічний Центр
Український державний університет залізничного транспорту
Citation: Волков О. А. Исследование теплодеформационного влияния при поверхностном упрочнении сталей термофрикционной обработкой / О. А. Волков // Восточно-Европейский журнал передовых технологий = Eastern-European Journal of Enterprise Technologies. – 2016. – Т. 2, № 5 (80). – С. 38-44.
Abstract: Описываются результаты изучения влияния термофрикционной обработки (ТФО) на структуру и свойства сталей с различным химическим составом. Представлены данные о распределении микротвердости по сечению образцов, фотографии микроструктур после ТФО. Показаны графики температурных полей на участке поверхности, прилегающей к кромке. Приведены данные о напряженном состоянии и фазовом составе поверхности после ТФО.
The paper deals with studying the heat deformation influence in the surface strain hardening of steels by thermofriction processing. The main objective of the work was to determine the relationship between the surface heating temperature during TFP, cooling rate, deformation, structure formation and properties of steels, hardened by TFP. The study solved the thermal conductivity problem, which allowed determining the surface heating temperature of samples of steels 15Kh11MF, 65G, U8A, Kh12M in TFP. The photographs of microstructures, which show changes over the cross section of the samples are presented. The presence of surface-hardened “white layer” with increased hardness is obvious, as evidenced by the prints of micro-hardness measurements. The data showed that the deformation mechanism of hardening in a short-term heating of the hardenable surface is predominant in TFP. It is also noted that the “deformed grained martensite” structure is formed, the hardness of which is more than twice the hardness of the martensite structure obtained in hardening of the proposed steels and can be considered as a type of nanostructure.
Appears in Collections:Кафедра "Матеріалознавство"

Files in This Item:
File Description SizeFormat 
VEJ_2016_2_5_Volkov_Issledovanie.pdf699,25 kBAdobe PDFView/Open
Show full item record  Google Scholar

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.