Khrypunov, G. S.Kopach, G. I.Dobrozhan, A. I.Mygushchenko, R. P.Kropachek, О. Y.Lyubov, V. M.2020-12-232020-12-232019Structure and optical properties of CdS polycrystalline layers for solar cells based on CdS/CdTe / G. S. Khrypunov [et al.] // Functional Materials. – 2019. – Vol. 26, № 1. – P. 23-26.https://repository.kpi.kharkov.ua/handle/KhPI-Press/49956Thin CdS films about 200-500 nm thick with stable hexagonal modification with 85-80 % transparency value respectively in the visible and infrared spectrum regions were investigated. The use of the FTO sublayer to obtain heterosystem glass/FTO/CdS by magnetron sputtering does not affect the phase composition of the cadmium sulfide layer and the width of the band gap (Eg = 2.42-2.44 eV). Cadmium sulfide thin films, obtained by direct current magnetron sputtering, can be used as a layer of a wide window layer in thin-film solar cells based on the CdS/CdTe heterosystem.Досліджено тонкі плівки CdS товщина порядку 200-500 нм стабільної гексагональної модифікації зі значенням коефіцієнта прозорості 85-80% відповідно у видимій та інфрачервоній області спектра.Використання підшару FTO для отримання гетеросистем скло / FTO / CdS магнетронним розпиленням на постійному струмі не впливає на фазовий склад шару сульфіду кадмію та значення ширини забороненої зони матеріалу (Eg = 2.42-2.44 eV). Тонкі плівки сульфіду кадмію, отримані методом магнетронного розпилення на постійному струмі, можуть бути використані в якості шару широкозонного вікна в тонкоплівкових сонячних елементах на основі гетеросистеми CdS/CdTe.encadmium sulfidedirect current magnetron sputteringthin filmsstructuresoptical propertiesArticledoi.org/10.15407/fm26.01.23