Стратийчук, Д. А.Туркевич, В. З.Колабылина, Т. В.Осипов, А. С.Смирнова, Т. И.2014-07-292014-07-292013Получение мелкодисперсных композитов в системе Салм. − Ti − Si / Д. А. Стратийчук [и др.] // Вестник Нац. техн. ун-та "ХПИ" : сб. науч. тр. Темат. вып. : Химия, химическая технология и экология. – Харьков : НТУ "ХПИ". – 2013. – № 57 (1030). – С. 70-74.https://repository.kpi.kharkov.ua/handle/KhPI-Press/7956This work is devoted to the study of phase interaction in the ternary Cdiamond – Ti – Si system and was conducted to determine the optimum conditions for the formation of high-strength diamondcontaining composites. By using high static pressure (7.7 GPa), it was shown that starting from 1500 °C the binder component Ti3SiC2 decomposes to form the fine dispersed TiC and high-pressure b-SiC phases. Obtained diamond based composite is characterized by high physic and mechanical characteristics and can be used for stone processing.Представленная работа посвящена изучению фазового взаимодействия в тройной системе Салм. − Ti – Si с целью определения оптимальных условий формирования высокопрочных алмазосодержащих композитов. Используя высокие статические давления (7,7 ГПа), было показано, что начиная с 1500 °С связующий компонент – Ti3SiC2 – распадается с образованием мелкозернистогоTiC и фазы высокого давления b-SiC. Полученный композит на основе Салм. характеризуется высокими физико-механическими характеристиками и может быть использован при камнеобработке.ruтермостойкие композитыалмазные микропорошкиаппарат высокого давлениякарбид титанакарбид кремниясверхтвёрдая керамикаArticle