Bykanova, V. V.Sakhnenko, N. D.Ved, M. V.Nikiforow, K. V.Maiba, M. V.2020-03-032020-03-032015Synthesis and photocatalytic activity of Ti/TinOm ∙ ZrxOy coatings for azo-dye degradation / V. V. Bykanova [et al.] // Сучасні проблеми електрохімії : освіта, наука, виробництво : зб. наук. пр. – Харків : НТУ «ХПІ», 2015. – С. 108-109.https://repository.kpi.kharkov.ua/handle/KhPI-Press/44733Anodic oxidation of ВТ1-0 titanium and E-125 zirconium alloy in aqueous electrolyte solutions based on H2SO4 and K4P2O7 was used to obtain oxide coatings composed of Zr/ZrO2, Ti/TiO2, and mixed oxide systems Ti/TinOm· Zr xOy with synergetic effect. It was established mixed oxide materials contain from 0.17 up to 2.1 % wt. of zirconium. The catalytic activity of the synthesized coatings in the oxidation reaction of the methyl orange azo-dye under UV irradiation was shown. The process rate constants and synergy factors for the mixed systems were calculated.Анодним оксидуванням сплаву титану марки ВТ1-0 та цирконію марки Е-125 у водних розчинах електролітів H2SO4 й K4P2O7 одержано оксидні покриви складу Zr/ZrO2, Ti/TiO2, а також змішані оксидні системи Ti/TinOm ∙ ZrxOy з синергетичним ефектом. Встановлено, що змішані оксидні матеріали містять від 0,17 до 2,1% мас. цирконію. Визначено каталітичну активність синтезованих покривів у реакції окиснення азобарвника метилового жовтогарячого під дією УФ-випромінювання, визначені константи швидкості процесу та фактори синергізму для змішаних систем.enazo compoundselectrochemical anodizingазосполукиелектрохімічне анодуванняArticle