Документ Structure and corrosion resistance of vacuum-arc multi-period CrN/Cu, ZrN/Cu and NbN/Cu coatings(2020) Postelnyk, H. O.; Sobol, O. V.; Stolbovoy, V. A.; Serdiuk, I. V.; Chocholaty, O.The structure and properties of vacuum-arc multi-period composite coatings of the MeN/Cu system (where Me is Cr, Zr, and Nb) are studied. It was found that at the smallest nanolayer thickness (about 8…10 nm) of composites in the layers of all systems, only a phase with an fcc lattice is formed, without a pronounced texture in the nitride layers. For ZrN and CrN, the phases with an fcc lattice are equilibrium, and for NbN, they are nonequilibrium. An increase in the thickness of nitride layers leads to the appearance of a texture in ZrN/Cu and CrN/Cu systems and the formation of an equilibrium ε-NbN phase in the layers of the NbN/Cu system. Tests for corrosion resistance in the environment of the formation of chloride ions showed that the coatings are anodic reaction. The best corrosion properties were obtained for coatings with the smallest layer thickness (about 8…10 nm).Документ Structure, Adhesion Strength and Corrosion Resistance of Vacuum Arc Multi-Period NbN/Cu Coatings(2020) Postelnyk, H. O.; Sobol, O. V.; Chocholaty, O.; Zelenskaya, G. I.The influence of deposition modes on the phase-structural state, corrosion resistance, and adhesive strength of vacuum-arc multi-period NbN/Cu coatings is studied. It was found that in thin layers (about 8 nm, in a constant rotation mode), regardless of the change in the pressure of the nitrogen atmosphere, a metastable δ - NbN phase forms (cubic crystal lattice of the NaCl type). At a layer thickness of ~ 40 nm or more, a phase composition changes from the metastable δ - NbN to the equilibrium ε - NbN phase with a hexagonal crystal lattice. In the presence of the ε - NbN phase in the niobium nitride layers, the highest adhesive strength is achieved with a value of LС5 = 96.5 N. Corrosion resistance tests have shown that for all the studied samples the corrosion process has mainly an anodic reaction. The highest corrosion resistance was shown by coatings obtained at a pressure of 7·10-4 Torr, with the smallest bias potential of -50 V and the smallest layer thickness; with a thickness of such a coating of about 10 microns, its service life in the environment of the formation of chloride ions is about a year.