New features of surface modification of magnesium alloys by microarc oxidation (MAO)

Abstract

The work investigates the features of forming MАO coatings on magnesium alloys. It is shown that due to the choice of electrolysis conditions (electrolyte composition, current density and oxidation time) the process of microarc oxidation in the microarc discharge mode is stably implemented. It has been established that as a result of MАO treatment, ceramic coatings containing phases of magnesium oxide MgO, spinel MgAl2O4, Mg2SiO4 and Mg3(РО4)2 are formed. The phase composition of the coatings is determined by the composition of the electrolyte. The electrolysis conditions studied in this work provide high hardness of the coatings, reaching 7500 MPa, as well as high corrosion resistance. The obtained results allow us to recommend MАO coatings obtained on magnesium alloys both as an outer (functional) layer with high adhesion to the substrate and as a sublayer for the subsequent application of protective coatings (varnishes, polymers, in particular polytetrafluoroethylene).

У статті досліджено особливості формування МДО-покриттів на магнієвих сплавах. Показано, що шляхом підбора умов електролізу (склад електроліту, щільність струму, час оксидування) стійко реалізується процес мікродугового оксидування в режимі мікродугових розрядів. Встановлено, що в результаті МДО-обробки формуються керамічні покриття, що містять такі фази, як оксид магнію МgO, шпінель MgAl2O4, сполуки Mg2SіO4 і Мg3(РО4)2. Фазовий склад покриттів визначається складом електроліту. Досліджені в роботі умови електролізу забезпечують високу твердість покриттів, яка досягає до 7500 МПа, а також високу корозійну стійкість. Отримані результати дозволяють рекомендувати МДО-покриття, отримані на магнієвих сплавах, як у якості зовнішнього (функціонального) шару з високою адгезією з основою, так і в якості підшару для наступного нанесення захисних покриттів (лаків, полімерів, зокрема політетрафторетилену).