Кафедри
Постійне посилання на розділhttps://repository.kpi.kharkov.ua/handle/KhPI-Press/35393
Переглянути
9 результатів
Результати пошуку
Документ Structural engineering and functional properties of vacuum-arc coatings of high-entropy (TiZrNbVHf)N and (TiZrNbVHfTa)N alloys nitrides(Institute for Single Crystals, 2019) Sobol, O. V.; Dur, Osman; Postelnyk, A. A.The effect of nitrogen pressure during the deposition of vacuum-arc (TiZrNbVHf)N and (TiZrNbVHfTa)N coatings on their phase-structural state, substructure and resistance to abrasive wear was investigated. It was established that in multi-element (based on high-entropy alloys) (TiZrNbVHf)N and (TiZrNbVHfTa)N coatings obtained in a nitrogen atmosphere in the range of nitrogen pressures PN = 2.5 ·10-4-4.5 ·10-3 Torr, a single-phase state is formed (based on cubic crystal lattice of structural type NaCl). The use of a multi-element composition with a single-phase state with a cubic lattice allows for (Ti-V-Zr-Nb-Hf-Ta)N coatings to achieve high microstrain values (up to 1.2 %) at low deposition pressure. It was found that high-entropy nitride coatings with low abrasive wear are characterized by a crystallite grain size of less than 50 nm, the absence or low level of texture perfection [111], and the presence of a rather high microstrain in crystallites (reaching 1.2 %). The reasons for the observed changes in the structural state and substructure of multi-element nitride coatings and their effect on abrasive resistance are discussed.Документ А Computer Simulation of Radiation-Induced Structural Changes and Properties of Multiperiod ZrNₓ/MoNₓ System(Sumy State University, 2017) Sobol, O. V.; Meylekhov, A. A.; Bochulia, T. V.; Stolbovoy, V. A.; Gorban, V. F.; Postelnyk, A. A.; Shevchenko, S. M.; Yanchev, A. V.Influence of the period value Λ (at different negative potential Ub that supplied during deposition) on phase composition, structure, stress-strain state and hardness of multiperiod coatings ZrNₓ/MoNₓ is investigated by using complex methods of validation structural state at combined with microindentation. Formation in layers ZrNx and MoNx the phases with cubic lattice and preferred orientation of crystallites with axis [100] is established. Stress-strain state of compression with increasing Ub is amplified and reaches maximum value (– 6.7 GPa) at Λ = 20 nm and Ub – 110 V. Hardness of coating increases with decreasing Λ from 300 to 20 nm. Coatings that obtained with Λ = 20 nm and Ub – 110 V have the highest hardness 44 GPa. Relaxation of structural compressive stresses and decreasing hardness is happening at smaller Λ and larger Ub – 110 V (as a result of radiation-stimulated forming defect and mixing). Data of computer modeling of defectiveness at atomic level at bombardment of ions that accelerated in field Ub are used to explain the results.Документ Багатошарові наноструктурні покриття для твердосплавного інструменту(EMKE Building, Budapest, 2020) Дубоносов, Володимир Леонідович; Кричковська, Лідія ВасилівнаРозробка зносостійких покриттів раніше залишається сьогодні основним напрямком підвищення надійності різального інструменту для сучасної металообробки. Від зміцнюючих покриттів вимагають підвищених характеристик твердості, що поєднуються з в'язкістю, міцної адгезією до підкладки, теплостійкістю, жаростійкістю і іншими якостями. До таких покриттів можуть бути віднесені багатошарові наноструктурні покриття (БНП) на основі різних нітридів. Змінюючи параметри їх нанесення, можна регулювати склад, структуру, морфологію, а також товщину і кількість окремих шарів в БНП. Високі значення твердості, стійкості до пластичної деформації визначають підвищену міцність адгезії їх з різними підкладками в порівнянні з покриттями, де багатошарова складова відсутня. Одним із шляхів вирішення проблеми стабілізації структури при високій температурі може бути формування додаткового бар'єрного шару на основі нітридів тугоплавких металів. Вирішення такого завдання поставлено в роботі.Документ Structural Engineering and Mechanical Properties of (Ti-V-Zr-Nb-Hf-Ta)N Coatings Obtained at Different Pressures(Сумський державний університет, 2019) Sobol, O. V.; Andreev, A. A.; Postelnyk, H. O.; Meylekhov, A. A.; Sagaidashnikov, Yu. Ye.; Stolbovoy, V. A.; Yevtushenko, N. S.; Syrenko, T. O.; Kraievska, Zh. V.; Zvyagolskiy, A. V.Effect of pressure of the reaction gas on the texture, structural stress state and mechanical properties (hardness and resistance to abrasive wear) in vacuum-arc coatings based on Ti-V-Zr-Nb-Hf-Ta nitrides of high entropy alloys were investigated in this work. At a bias potential of – 200V, an increase in nitrogen pressure during deposition from 2.5·10⁻⁴ to 4.5·10⁻³ Torr leads to an increase in the content of nitrogen atoms in the coating, and the formation of a bittexture state [111] + [311] is established. The formation of a biaxial texture occurs due to the presence in alloys of atoms with very different masses (Ti, V and Hf, Ta). The use of a multi-element composition in a single-phase state with a simple cubic lattice allows to achieve high values of microstrain (up to 1.4 %) with a low deposition pressure. It is determined that the increase of nitrogen pressure during deposition leads to an increase in macrostresses. The highest hardness of 53 GPa is achieved in coatings obtained at a pressure of 2·10⁻³ Torr. It has been established that coatings with high resistance to abrasive wear are found to be: crystallite grain size 12-25 nm, absent of texture (or a low level of texture perfection), and also rather high microstrain in crystallites.Документ Corrosion resistance of AISI 304 steel from compositional oxide coatings(Фізико-механічний інститут ім. Г. В. Карпенка Національної академії наук України, 2020) Shtefan, V. V.; Kanunnikova, Nadiia; Smyrnov, A.; Shepil, T.Документ Застосування сплаву цинк-нікель в технології цинкування(НТУ "ХПІ", 2019) Артеменко, Валентина Мефодіївна; Майзеліс, Антоніна ОлександрівнаБільш від’ємний потенціал цинкових покриттів забезпечує надійний захист сталевої основи від корозійного руйнування. Для підвищення хімічного опору корозійним процесам цинкові покриття обов'язково піддають завершальній обробці, наприклад, хроматуванню. Недоліками останнього є застосування токсичних сполук Cr (VІ) і зняття значного шар цинкового покриття (до 2 мкм). Мета досліджень полягала в обґрунтуванні вибору електроліту цинкування, який найбільшою мірою відповідає сучасним вимогам, а також в заміні хроматної плівки на тонкий шар цинк-нікелевого сплаву. Матеріали та методи дослідження. Виміри проводили в триелектродній комірці за допомогою потенціостату ПІ-50.1 з насиченим хлорид срібним електродом порівняння. Значення потенціалів електродів на графіках наведені за цим електродом. Цинкові покриття наносили з хлоридного, аміакатного та лужних електролітів з двома варіантами органічних добавок. Покриття сплавом цинк-нікель отримували з аміакатно-гліцинатного електроліту. Хлоридний та аміакатний електроліти характеризуються високими виходами за струмом, близькими до 100%, майже у всьому діапазоні густин струму від 1 до 4 А/дм². В лужних електролітах зі зростанням густини струму вихід за струмом знижується, що сприяє більшій рівномірності металевих покриттів. Оцінку розсіювальної здатності в досліджуваних електролітах проводили за допомогою ячійки Хулла з розбірним катодом. Співвідношення максимальних і мінімальних прирощень ваги на окремих секціях катоду в свідчить про більш високу розсіювальну здатність лужних електролітів. Завдяки високим захисним властивостям покриттів цинк-нікелевим сплавом пропонується в технологічному процесі цинкування осаджувати тонкий шар (0,5-0,7 мкм) цинк-нікелевого покриття з амонійно-гліцинатного електроліту замість хроматної пасивної плівки.Документ Исследования возможности использования шлама абразивного производства для покрытия изложниц(Національний технічний університет "Харківський політехнічний інститут", 2017) Бондаренко, Тамара Степановна; Горбенко, Вероника Владимировна; Васьковец, Людмила Антоновна; Питак, Олег ЯрославовичРазработаны научные основы осаждения жаростойких покрытий для защиты изложниц и на этой основе созданы новые покрытия стеклокерамического типа, обладающие высокозащитным действием, обеспечивающие повышение стойкости изложниц и улучшение качества материала.Документ Аналіз характеристик композиційних порошків для плазмового напилювання на основі ТіС – Ni(P) – Cu при розробці САПР ТП шліфування покриттів(НТУ "ХПІ", 2018) Тонконогий, В. М.; Сіньковський, А. С.; Рибак, О. В.У даній роботі наведені результати досліджень характеристик плазмових покриттів на основі композиційних порошків системи ТіС – Ni(P) – Cu у процесі їхнього шліфування та подальшої експлуатації. Випробовування проводились в умовах, у яких передбачається подальше використання деталей з цим покриттям. Була виявлена залежність міцності зчеплення покриття з основою, когезійної міцності і пористості та інших критично важливих характеристик таких покриттів від параметрів процесу їхнього нанесення. При дослідженні покриттів на основі ТіС – Ni(P) – Cu на зносостійкість за певних умов зношування не спостерігалось внаслідок явища вибіркового перенесення.Документ Моделі та властивості нових матеріалів на мікро- та нанорівні на прикладі покриттів на металах(НТУ "ХПІ", 2018) Грабовський, Андрій Володимирович; Ткачук, Микола Миколайович; Мейлехов, Андрій Олександрович; Постельник, Ганна Олександрівна; Глущенко, Марія Олександрівна; Князєв, Сергій АнатолійовичУ роботі наведено аналіз сучасного стану технологій та дослідження властивостей тонких покриттів на металі. Розглянуто функціональні, захисні та декоративні покриття на металах. Ці покриття поєднують у собі різноманітні властивості: захист від корозії, високу твердість та зносостійкість тощо. Розглянуті багатокомпонентні та багатошарові покриття. Проаналізовано на додаток вплив підготовки поверхні підкладки перед осадженням покриття. Проведено також дослідження впливу потенціалу, поданого на підкладку, і зміни відстані "підкладка-катод" на процеси осадження, розпилення, а також механічні характеристики у процесі очищення поверхні сталі ніобієм.