Кафедри
Постійне посилання на розділhttps://repository.kpi.kharkov.ua/handle/KhPI-Press/35393
Переглянути
3 результатів
Результати пошуку
Документ Magnetoresistance of Polycrystalline Bi₁₋ₓSbₓ Alloys (x = 0 – 0.07)(IEEE, 2017) Doroshenko, A. N.; Martynova, K. V.; Rogacheva, E. I.A detailed investigation of the composition dependences of magnetoresistance for polycrystalline Bi₁₋ₓSbₓ solid solutions in a concentration range x = 0 – 0.07 was performed at 300 K in weak and strong magnetic field. It was shown that the composition dependences of magnetoresistance are clearly expressed nonmonotonic type. The presence of concentration anomalies of magnetoresistance was confirmed that had been earlier observed in the range x = 0 – 0.1 on cast samples after different kinds of thermal treatment and interpreted as a manifestation of electron phase transitions. It is shown that the position of the extrema does not depend on the magnitude of the magnetic field in the interval 0.01 - 1.0 T.Документ Thermoelectric properties of polycrystalline Bi₁₋ₓSbₓ solid solutions in the concentration range x = 0 – 0.25(National Academy of Sciences of Ukraine, 2016) Doroshenko, A. N.; Rogacheva, E. I.; Drozdova, A. A.; Martynova, K. V.; Men'shov, Yu. V.A detailed investigation of the dependence of thermoelectric properties of polycrystalline Bi₁₋ₓSbₓ solid solutions on composition in a wide concentration range (x = 0 – 0.25) was performed at room temperature. The objects of study were cast samples of various composition obtained by ampoule method in one technological cycle consisting in cooling of ampoules with melts in the air and subsequent long homogenizing annealing at temperature (520 ± 5) K for 720 hours. It was shown that the composition dependences of properties are of clearly expressed nonmonotonic type. The presence of concentration anomalies of thermoelectric properties was confirmed that had been earlier observed in the range x = 0 – 0.1 on cast samples after different kinds of thermal treatment and interpreted as manifestation of electron phase transitions. A complicated nature of dependences at x > 0.1 is attributable to qualitative changes in Bi₁₋ₓSbₓ band structure at certain critical compositions, a change in relative contribution to conductivity of charge carriers from different energy bands with a change in antimony concentration and high sensitivity of energy spectrum and physical properties of Bi₁₋ₓSbₓ к to external effects.Документ Термоэлектрические свойства поликристаллических твердых растворов Bi₁₋ₓSbₓ в интервале концентраций x = 0-0.25(Інститут термоелектрики НАН України, 2016) Дорошенко, А. Н.; Рогачева, Елена Ивановна; Дроздова, Анна Анатольевна; Мартынова, К. В.; Меньшов, Ю, В.Проведено детальное исследование зависимости термоэлектрических свойств поликристаллических твердых растворов Bi₁₋ₓSbₓ от состава в широком интервале концентраций (x = 0-0.25) при комнатной температуре. Объекты исследования – литые образцы различного состава, полученные ампульным методом в одном технологическом цикле, состоящем в охлаждении ампул с расплавами на воздухе и последующем длительном гомогенизирующем отжиге при температуре (520 ± 5) К в течение 720 часов. Показано, что зависимости свойств от состава носят отчетливо выраженный немонотонный характер. Подтверждено наличие концентрационных аномалий термоэлектрических свойств, наблюдаемых ранее в интервале x = 0-0.1 на литых образцах после других видов термической обработки и интерпретируемых как проявление электронных фазовых переходов. Сложный характер зависимостей при x > 0.1 объясняется качественными изменениями в зонной структуре Bi₁₋ₓSbₓ при определенных критических составах, изменением относительного вклада в проводимость носителей заряда из различных энергетических зон при изменении концентрации сурьмы и высокой чувствительностью энергетического спектра и физических свойств Bi₁₋ₓSbₓ к внешним воздействиям.