Electrochemical oxidation of VT6 titanium alloy in oxalic acid solutions

Abstract

The influence of the electrolysis parameters on the process of VT6 titanium alloy oxidizing in oxalic acid solutions is presented. It is shown that the nature of cell voltage-time curves for the alloy samples depends on the current density used. The interference-colored oxide films are formed on the surface of the alloy at the anodic current density above 0.5 A∙dm⁻². The maximal thickness and the oxide film color are determined by the cell voltage and do not depend on other electrolysis parameters. The results of oxidation in oxalic and sulfuric acids solutions made it possible to establish the similarity of cell voltage-time dependencies and the time of oxide film formation with maximal thickness for these electrolysis conditions.Приведені результати дослідження впливу параметрів електролізу на процес оксидування титанового сплаву ВТ6 у розчинах оксалатної кислоти. Показано, що характер формувальних залежностей зразків сплаву залежить від величини використаної густини струму. За анодної густини струму вище 0,5 A∙дм⁻² на поверхні сплаву утворюються інтерференційно-забарвлені оксидні плівки. Гранична товщина та колір оксидної плівки визначаються напругою формування і не залежать від інших параметрів електролізу. Результати оксидування в розчинах оксалатної та сульфатної кислот дали можливість встановити збіг формувальних залежностей сплаву і часу утворення оксиду максимальної товщини для даних умов електролізу.