Magnetoresistance of Polycrystalline Bi₁₋ₓSbₓ Alloys (x = 0 – 0.07)
Дата
2017
DOI
doi.org/10.1109/YSF.2017.8126618
Науковий ступінь
Рівень дисертації
Шифр та назва спеціальності
Рада захисту
Установа захисту
Науковий керівник
Члени комітету
Назва журналу
Номер ISSN
Назва тому
Видавець
IEEE
Анотація
A detailed investigation of the composition dependences of magnetoresistance for polycrystalline Bi₁₋ₓSbₓ solid solutions in a concentration range x = 0 – 0.07 was performed at 300 K in weak and strong magnetic field. It was shown that the composition dependences of magnetoresistance are clearly expressed nonmonotonic type. The presence of concentration anomalies of magnetoresistance was confirmed that had been earlier observed in the range x = 0 – 0.1 on cast samples after different kinds of thermal treatment and interpreted as a manifestation of electron phase transitions. It is shown that the position of the extrema does not depend on the magnitude of the magnetic field in the interval 0.01 - 1.0 T.
Опис
Ключові слова
bismuth-antimony solid solution, composition, magnetoresistance, electronic transition, critical phenomena, твердий розчин вісмут-сурма, композиція, магнітоопір, електронний перехід, критичні явища
Бібліографічний опис
Doroshenko A. N. Magnetoresistance of Polycrystalline Bi₁₋ₓSbₓ Alloys (x = 0 – 0.07) [Electronic resource] / A. N. Doroshenko, K. V. Martynova, E. I. Rogacheva // International Young Scientists Forum on Applied Physics and Engineering (YSF) : proc. of the conf., October 17-20, 2017. – Electronic text data. – Lviv, 2017. – P. 199-202. – Access mode: https://ieeexplore.ieee.org/abstract/document/8126618/similar, free (date of application 21.12.2022).